Young's modulus | 1600 | MPa |
Tensile strength | 40 | MPa |
Elongation | 2.5 | % |
Compressive strength | 165 | MPa |
Fatigue | 7.5 | MPa |
Bending strength | 45 | MPa |
Hardness | 90.5 | Janka |
Yield strength | 0 | MPa |
Thermal expansion | 115 | E-6/K |
Thermal conductivity | 0.21 | W/m*K |
Specific heat | 1380 | J/kg*K |
Melting temperature | 210 | °C |
Glass temperature | 70 | °C |
Minimum service temperature | -40 | °C |
Maximum service temperature | 75 | °C |
Density | 1300 | kg/m3 |
Resistivity | 1E+17 | Ohm*mm2/m |
Breakdown potential | 37 | kV/mm |
Dielectric loss factor | 0.0095 | |
Friction coefficient | 0 | |
Refraction index | 1.49 | |
Shrinkage | 0.55 | % |