LCP

Liquid Crystal Polymer

Young's modulus 25000 MPa
Tensile strength 180 MPa
Elongation 4.6 %
Compressive strength 80 MPa
Bending strength 220 MPa
Impact strength 2.915 J/cm
Yield strength 0 MPa
Thermal expansion 55 E-6/K
Melting temperature 345 °C
Minimum service temperature -100 °C
Maximum service temperature 260 °C
Density 1235 kg/m3
Resistivity 1E+19 Ohm*mm2/m
Breakdown potential 37 kV/mm
Dielectric loss factor 0.0035
Friction coefficient 0.4
Shrinkage 0.6 %
Water absorption 0.06 %