SAN - Styreenacrilonitril
| Property | Min | Max | Unit |
| Young's modulus | 3500 | 3800 | MPa |
| Shear modulus | 1380 | 1380 | MPa |
| Tensile strength | 70 | 80 | MPa |
| Elongation | 3 | 4 | % |
| Fatigue | 27 | 27 | MPa |
| Bending strength | 110 | 140 | MPa |
| Hardness | 80 | 80 | Rockwell |
| Impact strength | 0.2 | 0.3 | J/cm |
| Thermal expansion | 60 | 80 | e-6/K |
| Thermal conductivity | 0.15 | 0.15 | W/m.K |
| Specific heat | 1180 | 1180 | J/kg.K |
| Glass temperature | 97 | 105 | C |
| Service temperature | -20 | 90 | C |
| Density | 1060 | 1080 | kg/m3 |
| Resistivity | 1E+20 | 1E+20 | Ohm.mm2/m |
| Breakdown potential | 150 | 170 | kV/mm |
| Dielectric loss factor | 0.00001 | 0.00008 | |
| Friction coefficient | 0.52 | 0.52 | |
| Refraction index | 1.565 | 1.569 | |
| Thickness | 0.8 | 6.3 | mm |
| Shrinkage | 0.4 | 0.7 | % |
| Water absorption (at 50% hum.) | 0.2 | 0.6 | % |