ZrO2-Y2O3 - FSZ (EN)

ZrO2/Y2O3 - FSZ

Youngs modulus 150000MPa
Tensile strength 0MPa
Compressive strength 2000MPa
Bending strength 250MPa
Hardness 1200Vickers
Yield strength 0MPa
Thermal expansion 10E-6/K
Thermal conductivity 2.5W/m*K
Specific heat 500J/kg*K
Minimum service temperature 0°C
Maximum service temperature 2000°C
Density 5800kg/m3
Resistivity 10-15/3.0Ohm*mm2/m
Friction coefficient 0
Main constituent 90
Average grain size 2.5μm
Fracture toughness 6MN/m3/2